Reflective Films
Reflective Films for Direct LED
- SY260&SY750 is a reflection film for LCD backlights with excellent reflectivity and light scattering.
- SY750 is suitable for high luminance applications with high reflectivity.
| Property | Unit | SY260 | SY750 | Measured | |
|---|---|---|---|---|---|
| General | Thickness | ㎛ | 188 | 188 | SKC HT&M Method |
| Mechanical | Tensile Strength(MD/TD) | Kg/㎟ | 13.5/13.1 | 8.6/9.2 | ASTM D 882 |
| Elongation at Break(MD/TD) | % | 130.0/110.0 | 101.8/82.0 | ASTM D 882 | |
| Optical | Reflectance (@550nm) | % | 96.2 | 97.9 | SKC HT&M Method |
| Light Transmission | % | 2.7 | 2.7 | ASTM D 1003 | |
| Gloss 60º (Inside/Outside) | degree | 25/24 | 27/26 | ASTM D 523 | |
| Thermal | Heat Shrinkage(MD/TD) | % | 3.0/2.0 | 1.6/1.3 | SKC HT&M Method(150℃×30 min) |
| Cross Sectional Image | SEM | ||||
This Information is the best currently available on the subject. The results should, however, only be regarded as a general guide to material properties and not as a guarantee. Some of the properties can be changed as a result of supplier's efforts to improve the quality or production efficiency of the subject.
Reflective Films for Edge LED
- The coating reflector film protects the light guide plate (LGP) from damage between the reflective sheet surface and LGP,and improves the uniformity of the display screen
- It shows excellent light scattering effect through improved uniformity of the light surface.
| Property | Unit | RL603LA | RL703LA | RL603GA | Measured | |
|---|---|---|---|---|---|---|
| General | Thickness | ㎛ | 210 | 210 | 210 | SKC HT&M Method |
| Mechanical | Tensile Strength(MD/TD) | Kg/㎟ | 13.5/13.1 | 8.6/9.2 | 13.5/13.1 | ASTM D 882 |
| Elongation at Break(MD/TD) | % | 130.0/110.0 | 101.8/82.0 | 130.0/110.0 | ASTM D 882 | |
| Optical | Reflectance (@550nm) | % | 96.2 | 97.9 | 96.2 | SKC HT&M Method |
| Light Transmission | % | 2.7 | 2.7 | 1.5 | ASTM D 1003 | |
| Gloss 60º (Coated Side) | degree | 40 | 40 | 10 | ASTM D 523 | |
| Thermal | Heat Shrinkage(MD/TD) | % | 3.0/2.0 | 1.6/1.3 | 3.0/2.0 | SKC HT&M Method (150℃×30 min) |
| Cross Sectional Image | SEM | |||||
This Information is the best currently available on the subject. The results should, however, only be regarded as a general guide to material properties and not as a guarantee. Some of the properties can be changed as a result of supplier's efforts to improve the quality or production efficiency of the subject.